This document describes procedures for measuring average grain size derived from a two-dimensional polished cross-section using electron backscatter diffraction (EBSD). This requires the measurement of orientation, misorientation and pattern quality factor as a function of position in the crystalline specimen[1]. The measurements in this document are made on two dimensional sections. The reader should note carefully the definitions used (3.3) which draw a distinction between the measured sectional grain sizes, and the mean grain size which can be derived from them that relates to the three dimensional grain size.
NOTE 1 While conventional methods for grain size determination using optical microscopy are well-established, EBSD methods offer a number of advantages over these techniques, including increased spatial resolution and quantitative description of the orientation of the grains.
NOTE 2 The method also lends itself to the measurement of the grain size of complex materials, for example those with a significant duplex content.
NOTE 3 The reader is warned to interpret the results with care when attempting to investigate specimens with high levels of deformation.
Informations générales
-
État actuel: PubliéeDate de publication: 2020-07Stade: Norme internationale publiée [60.60]
-
Edition: 2
-
Comité technique :ISO/TC 202ICS :71.040.50
- RSS mises à jour
Cycle de vie
-
Précédemment
AnnuléeISO 13067:2011
-